Corresponding foreign brands: American Kenrich Petrochemicals Inc. KR-12
Main chemical components: 
Physical and chemical properties:
| Appearance | yellow transparent viscous liquid |
| Flash point | 105℃ |
| Density: ρ (20℃) | 1.031 |
| Refractive index n 20℃ | 1.465 |
| Decomposition temperature | 260℃ |
| Soluble | isopropyl alcohol, xylene, toluene, mineral oil, and hydrolyzes with water to precipitate |
This product is a non-toxic and non-corrosive liquid. The oral poisoning of rats is LD 50 30g/kg (reference value: table salt LD 50 3.8g /kg) Compatible with semi-polar materials
Application areas:
Plastic products, rubber products, adhesives, FRP products, paints, inks, ointments, magnetic materials, waterproof materials, composite flame retardants, etc.
Application object:
1. Matrix resin: PE, PP, PS, PC, AS, ABS, PVC, SBS, polyester, polyether, polyurethane, polyamide, polycarbonate and other thermoplastic, thermosetting resins and other elastomers.
2. Inorganic fillers: CaCO3, MgCO3, BaSO4, CaSO4, MgO, Al(OH)3, talc powder, mica powder, lithopone powder, titanium dioxide, wollastonite powder, pyrophyllite powder, sepiolite powder, Carbon black, clay, bentonite, aluminum smelting red mud, iron red, chrome yellow, titanium cyanine blue, antimony trioxide, ammonium polyphosphate, zinc metaborate, etc.
Product Features:
1. This product is a monoalkoxy titanate coupling agent, suitable for dry inorganic fillers containing only physically bound water and chemically bound water. Such as: titanium dioxide, CaCO3, iron red, chrome yellow, titanium cyanine and other pigments.
2. This product has partial flame retardancy and thermal stability, and is a PVC flexible agent and a viscosity reducing agent for epoxy resin.
3. This product has excellent dispersion and anti-settling effects on pigments such as titanium dioxide and iron red. For details, please refer to "Coating Dispersion Coupling Agent".
4. Use HY-102 to change TiO2 in polyamide cross-linked epoxy paint Filling amount with clay. (See Table 1-1)
5. This product can greatly increase the filling amount of inorganic filler in resin (plastic, rubber, paint and other composite products), significantly improve the tensile strength and impact strength of the product, Physical and mechanical properties such as elongation at break, reduce system viscosity, improve processing performance, reduce energy consumption and production costs.
Physical and chemical properties:
This product is yellow transparent viscous liquid, flash point 105℃, density: ρ (20℃): 1.031, refractive index n 20℃ 1.465, decomposition temperature 260℃. It is soluble in isopropyl alcohol, xylene, toluene, mineral oil, and hydrolyzes with water to precipitate. This product is a non-toxic and non-corrosive liquid. The oral poisoning of rats is LD 50 30g/kg (reference value: table salt LD 50 3.8g /kg) Compatible with semi-polar materials
| Formula, constant pigment volume concentration | 1 | 2 | 3 |
| Epoxy, intermediate molecular weight 18000cqs | 6 | 6 | 6 |
| TiO 2 , rutile | 3 | 2 | 1.5 |
| Mixed solvent: 65% xylene, 35% MIBK | 2.5 | 2.5 | 2.5 |
| Soybean Lecithin | 0.05 | - | - |
| Clay (ASP-170) | - | 0.7 | 1.05 |
| HW-102 | - | 0.024 | 0.023 |
| Total measurement | 11.55 | 11.224 | 11.073 |
| Ball milling time | 30 | 15 | 15 |
| Light protection | very good | Better than 1 | Equivalent to 1 |
| Glossy Gardner 60F | >90 | >90 | >90 |
| Relative ball mill auxiliary costs | 1 | 0.73 | 0.59 |
| % Replace TiO 2 with filler | no | 30 | 50 |
Table 1-1