Isopropyl trioleate acyloxy titanate HY-105

Corresponding foreign brands: American Kenrich Petrochemicals Inc. OL-T951; KR-2

Main chemical components:

Physical and chemical properties:

Appearance	wine red transparent viscous liquid
Flash point	100℃
Density: ρ (20℃)	0.934
Refractive index n 20℃	1.477
Decomposition temperature	255℃
Soluble	isopropyl alcohol, xylene, toluene, mineral oil, and hydrolyzed and precipitated by reaction with water

 This product is a non-toxic and non-corrosive liquid. The oral poisoning of rats is LD 50 30g/kg (reference value: table salt LD 50 3.8g /kg) Compatible with semi-polar materials.

Application areas:

Plastic products, rubber products, adhesives, FRP products, paints, inks, ointments, magnetic materials, waterproof materials, composite flame retardants, etc.

Application object:

1. Matrix resin: PE, PP, PS, PC, AS, ABS, PVC, SBS, polyester, polyether, polyurethane, polyamide, polycarbonate and other thermoplastic, thermosetting resins and other elastomers.
2. Inorganic fillers: CaCO₃, MgCO₃, BaSO₄, CaSO₄, MgO, Al(OH)₃, talc powder, mica powder, lithopone powder, titanium dioxide, wollastonite powder, pyrophyllite powder, sepiolite powder, Carbon black, clay, bentonite, aluminum smelting red mud, iron red, chrome yellow, titanium cyanine blue, antimony trioxide, ammonium polyphosphate, zinc metaborate, etc.

Product Features:

1. This product is a monoalkoxy titanate coupling agent, suitable for the treatment of dry inorganic fillers containing only physically bound water and chemically bound water. Such as calcium carbonate, aluminum hydroxide, antimony trioxide, etc.
2. This product can significantly improve the surface finish of the product and increase the dimensional stability.
3. This product is used in carbon black paint to shorten the grinding and dispersion time by more than 1/3. The semi-finished black slurry is placed for one month without roughing, and the black slurry without the coupling agent returns to roughness within a week.
4. Effectiveness of application in PE cross-linked foamed shoe pieces (see Table 1-1)
5. Application of light CaCO₃ treated with HW-105 on PVC microcellular foam slippers (see Table 1-2)
6. This product can greatly increase the filling amount of inorganic filler in resin (plastic, rubber, paint and other composite products), significantly improve the physical and mechanical properties of the product such as tensile strength, impact strength, elongation at break, reduce system viscosity, improve Processing performance, reduction, energy consumption and production costs.

Test items	skills requirement	10 original production samples	New production samples (after HW-105 processing)
		3 servings of light CaCO	20 servings	30 servings	40 copies
Tensile strength (Mpa)	≥2.5	4	3.9	3.8	3.6
Elongation(%)	≥150	302	276	276	254
Shore Hardness (degrees)	45±5	61	66	65	65
Density (g/cm3)	0.33-0.43	0.3	0.33	0.33	0.32
Flex cracking (times)	More than 60,000 times	qualified	qualified	qualified	qualified

Table 1-1

Test items	GB3807-83	Sample A	Sample B	Sample C	Original sample
	standard	50 copies	50 copies	50 copies	CaCO 3 20 servings
Tensile strength (Mpa)	≥2.1	3.25	2.35	2.47	2.2
Relative elongation (%)	≥130	149	135	138	130
Shore Hardness (degrees)	18-30	29	25	twenty three	18
Density (g/cm3)	0.25－0.4	0.38	0.34	0.3	0.29

Table 1-2

Note: Samples A, B, and C have all been processed by HW-105.